الوصف

Related Standard:

1. EN ISO ****3 - 4 Glass in building -Laminated glass and laminated safety glass - Part 4: Test methods for durability Clause 5 High-temperature test
2. AS/NZS ***8 Safety glazing materials in buildings Appendix F Boil Test
3. GB ****3.3 Safety glazing materials in building Part 3:Laminated glass Clause 7.8 Heat resistance test
4. ANSI Z*7.1 Safety Glazing Materials Used in Buildings - Safety Performance Specifications and Methods of Test - Clause 5.3.2 ( 1 ) Boil Test

5. Power: **0V *0Hz 3Kw (Customized)
6. Outside Size: **0mm***0mm***5 mm
7. Inner Size: **0mm***5mm***0mm
8. Rack：**0mm***5mm***0mm
9. At most 6 samples with **0mm***0mm

1. Determining the effect of exposure of safety glazing materials to temperature and humidity condition by boiling

1.  Specimens are immerse in hot water and boiling water for specified period of time and inspect bubbles and others defects

1. The apparatus include two water baths, each of sufficient size to hold the test specimen fully immersed vertically on edge for the duration test.

1. Three specimen of size **0mm***0mm manufacture in a manner identical with impact test specimens and of like thickness shall be tested.
2. These specimens may be cut from production samples of the size and thickness submitted for impact testing.
3. For heat strengthened or toughened laminated glass, test specimen may be cut from a similar original sheet of annealed laminated glass

1. Immerse the specimens vertically on edge in a bath of water maintained at a temperature of *6°C±3°C for 3 min
2. Quickly transfer the specimens to a bath of water maintain at boiling point. Immerse the specimens vertically on edge for 2 h
3. Remove the specimens and examine for the bubbles and others defects