Physical Properties

Test Method

Nominal Value

Unit

Density

ISO ***3

0.**1

g/cm3

Melt Mass-Flow Rate (MFR)

ISO ***3

1.9

g/*0min

Hardness

Shore Hardness (shore D)

ISO **8

*5

Mechanical Properties

Tensile Modulus

ISO ****2

**5

MPa

Tensile Strength

Yield, 

ISO ****2

9.0

MPa

Break,

*3.0

MPa

Tensile Strain(Break)

ISO ****2

**0

%

Modulus of Elasticity

Internal Method

**0

MPa

Thermal

Vicat Softening Temperature

ISO **6/A*0

*9.0

°C

Melting Temperature (DSC)

DIN ****5

**8

°C

Peak Crystallization Temperature (DSC)

DIN ****5

*7.0

°C

Heat of Fusion

DIN ****5

**0

J/g

Electrical

Volume Resistivity

ASTM D**7

8.5E**5

ohm •cm

Dielectric Strength

ASTM D**9

*0.0

kV/mm

Dielectric Constant (*0Hz)

ASTM D**0

2.*0

%

Dissipation Factor (*0 Hz)

ASTM D**0

0.****0