Metallized BOPP Capacitor Film

الوصف

* Products:

 Aluminum metalized polypropylene film.

 Aluminum-Zinc alloy metalized polypropylene film.

 Aluminum-Zinc alloy metalized polypropylene film with heavy edge.

* Cores:                              

  Material: Plastic

  Width: Film Slit Width +/*0.2mm

  Inner Diameter: *5mm *1.0mm/ *0.5mm

* Roll Outer Diameter:

  For slit widths 4.0mm up: **5 *6/**5mm

  For slit widths *0.0mm up: **0 *8/**8mm

  For slit widths *5.0mm up: **0 **0/**0mm

* Rolls:

  Film is wound on solid cores, with the metalized layer inside.

  Rolls are wound up to the specific outer diameter.

  The loose end of film is held in place by a closing sticker.

  Rolls are always packed in pairs.

  There is plastic foam between the rolls to protect the electrode side.

* Packing:

  Inner:

  The piled rolls are packed in plastic bag and heat-sealed with desiccants after vacuum removal.

  Labels inside the bags mark film type, thickness, width, free margin width and resistance.

  Outer:

  The bags are packed in carton cases.

  The carton cases are packed in wooden cases or reinforced carton.

* Storage:

 1.Film should be stored in its original packing until use. The temperature should be controlled to 5 - *5oC and humidity less than *5%RH.

 2. On exposure to moisture, the thin metalized layer is likely to be easily oxidized. Therefore, after the packing is opened, the rolls should be used as soon as possible.

 3. It is recommended that the opened rolls be stored in temperature conditions of *5 **5oC and humidity of less than *0%RH.

 4. Film kept sealed in the original packing and stored as described above is guaranteed according to the following conditions:

  Al metalized Film: *2 months from the delivered date.

  Al/Zn Alloy metalized Film: As Zn is relatively unstable; preservation period depends on the resistance of the film:

    *0 Ohms or less     6 months (from delivery date)

   *0 to*5 Ohms        3 months (from delivery date)

   *5 Ohms      1 month (from delivery date)