RTV*2 mold making silicone  applications

 RTV*2 mold making silicone  

is primarily intended for poly resin crafts, PU crafts, PU resin crafts ,gypsum crafts ,unsaturated resin crafts, lighting and candles crafts ,plastic toy , stationery gifts crafts industry, a large statue Buddha, furniture, furniture decorative materials, statues Buddha, artifacts copied, building decoration materials, largescale cement mold, artificial fossils Factory, Europe component factory,

simulation landscapes, animals and plants sculpture, sandstone crafts and so on.

RTV*2 mold making silicone description

RTV*2 mold making silicone is white or red flowing liquid with general hardness of ****0 shore A after curing. tin cured RTV silicone rubber  is a kind elastic silicon rubber mold which features with resistance to deformation, high-temperature, acid-alkali and expansion as well as high reproduction times, good tensile strength, tear strength and elongation.

FAQ. Why the RTV*2 mold making silicone just can be reproduced for a few times?

It can be due to the following reasons:

a. Adding too much silicone oil in to silicon rubber. Silicon oil is an additive which destroies the molecular weight of silicone rubber and reduce the tension and tear strength.

b. Using the silicon rubber with a high hardness to make molds for small sized products with delicate and intricate designs and the silicon rubber with a low hardness to makes molds for large sized products with simple designs.

(Notes: we should choose the silicon rubber specifically according to the requirements of our products to avoid this problem.)

Datesheet of   RTV*2 mold making silicone.

The proportions and reactions of the curing agent and the silicon as follows

a. Adding curing agent 1%, The RTV*2 mold making siliconecan still be operated within 2.5 hours and can be demoulded after **8 hours.
b. Adding curing agent 2%, The RTV*2 mold making siliconecan still be operated within *0 minutes to 1 hour and can be demoulded after **3 hours.
c. Adding curing agent 3%,  The RTV*2 mold making silicone can still be operated within *8 - *0 minutes and can be demoulded after 1.**2 hours.d. Adding curing agent 4%,  The RTV*2 mold making silicone can still be operated within *0 - *5 minutes and can be demoulded after 1 *1.5 hours
 