***-SIGHT GLASS***-

Material:Borosilicate glass

Usage: it is used in lever gauge in boiler for water position.

category:

B4, B5, B6, B7, B8, B9, B*0, B*1

A4, A5, A6, A7, A8, A9, A*0, A*1

1 Three tendons (4 grooves)

**0 x *4(*0) x *7mm; **0 x *4(*0) x *7mm; **0 x *4(*0) x *7mm;

**0 x *4(*0) x *7mm; **8 x *4(*0) x *7mm; **0 x *4(*0) x *7mm;

**5 x *4(*0) x *7mm; **0 x *4(*0) x *7mm; **5 x *4(*0) x *7mm;

**0 x *4 x *7mm; **0 x *4 x *7mm; **0 x *4 x *7mm;

**0 x *4 x *7mm; **0 x *4 x *7mm; **0 x *4 x *7mm;

2 Two tendons (3 grooves)

**0 x *4 x *7mm; **0 x *4 x *7mm; **0 x *4 x *7mm;

**0 x *4 x *7mm; **8 x *4 x *7mm; **0 x *4 x *7mm;

**5 x *4 x *7mm; **0 x *4 x *7mm; **5 x *4 x *7mm;

**0×*4×*2mm; **0×*8×*7mm; **0×*4×*0mm; **0×*4×*2mm;

3  Transparent plane

**0 x *4 x *7mm; **0 x *4 x *7mm; **0 x *4 x *7mm;

**0 x *4 x *7mm; **8 x *4 x *7mm; **6 x *4 x *7mm;

**0 x *4 x *7mm; **5 x *4 x *7mm; **5 x *4 x *2mm;

**8 x *8 x *3mm; **0 x *8 x *3mm; **5 x *8 x *3mm;

The other size is optional or according to the requirements of customers.

Working temperature: **0 °C, Working pressure: **8.0MPa

Physical Property:

1. Appearance

1) Air bubble: 

Diameter≤0.5mm, in the *0mm x *0mm area the quantity must be ≤3.Diameter from 0.5mm to 1.5mm dispersive air bubble, there is less 2 on the sight plane and less 5 on the No-sight plane. Their distance must be *0mm.

The air bubble of Diameter from 1.5mm to 2mm ≤3 on the No-sight plane. Their distance must *0mm.

On the sight plane, The distance to the side in 7.5mm,the air bubble of the  diameter1mm mustnt be more 2.

2) The glass dont allow slag and scrap iron, etc. impurity.

3) Stripe: dont allow have palpable filaceous and pectinate stripe on the sight plane.

4) Cockle: In the side face, dont allow have the cockle of depth1mm.

5) Crack: dont allow have crack.

6) Scrape: On the sight plane and in the 7.5mm to edge, the scrape of less than *0mm dont allow more 2 strips.

7)The sight plane must be polishing, and sealing side must be rubbing and polishing.

2. Color and Lustre 

It should be no color and transparent,and with its self tine green is allowed.

3. Water-resistance

Cooked in the water for 5 hours, then weigh up, then titration with *5ml    0~*1ug/g

4. Alkali-resistance

Cooked in the 0.5N NaOH for 3 hours,then Weigh up,weightlessness should be 

5. Temperature-resistance impacts capability

Put it into electric cooker, keep for 7min under the temperature of **0±1, then, put into the water of *0±1,it should not crack

6. Bend-resistance>/=*0MPa