Description
Capacity: from ****0 cubic meter to **0, **0 cubic meters per
year.
Equipments: stocking raw materials, mixing, molding, forming,
cutting, evaporating and curing, crane cramp, transporting
etc.,
1 Product weight is according to **0kg/m3 to control.
2 annual capacity **0, **0M3.
3 set raw material proportion: cement 6.5%, raw lime *3%, flyash
*8%, gypsum 3%, aluminum paste powder **0g/M3.
4 water and material rate 0.**1
5 one mould product 2.*8M3
6 Casting slurry cycle time **6 minutes, cut cycle time 5
minutes.
7 casting slurry temperature ****2 degree
8 body quiet stop. Time is 1.**2.5housr, temperature ****0 degree,
after quiet stop body strength is 0.***0.*8Mpa
9 Steam curing cycle time, come in and out autoclave about 0.5hour,
steam curing cycle time about is 6 hours/1.6Mpa, total 6.5
hours.
*0.
Cement lime fly ash style aerated block raw material proportion
name unit Cement lime fly ash
flash % ****0
cement % ***5
lime % ****5
gypsum % **5
Aluminum powder paste(**0kg/m3) 1/****0 8
Water & material rate 0.***0.*5
Casting system OC ****0
Aluminum mixing time S ****0
*1. Cement lime Sand style aerated block raw material
proportion
Name Unit Cement Lime Sand
Sand % ****5
Cement % ****0
Lime % ****0
Gypsum % **3
Aluminum powder paste(**0kg/m3) 1/****0 8
Water & material rate 0.***0.*5
Casting system OC ****8
Aluminum mixing time S ****0
Reference: cement is *2.5 Portland or *2.5 common cement
Aluminum power paste calculate to use according to **0kg/m3