Description
1. Properties Features:
(1). A lot of dispersed TiB2, TiAl3, AlB2 and TiC corpuscles
with high melting point are produced in the molten Aluminum
as foreign crystalline cores when these corpuscles coagulate,
notably refining the crystalline configuration of the cast ingots,
improving the general mechanic properties of the aluminum
cast.
(2). Less wastage, improve the quality of the surface, and
raise the uniformity degree of chromatic oxidation and
brightness.
2. Scope of Application:
Apply to the grain-refining of pure aluminum or aluminum
alloys in the course of smelting.
3. Operation Instructions:
(1). Temperature: **0~**0℃
(2). Dosage: aluminum: 0.8～1.5kg /T, aluminum
section: 0.5～1.0kg/T, aluminum alloys: 1～2kg/T
(3). Valid period for grain-refining: 6~8
hours.
(4). Operation method: Skim off the dross,
putAlTi5B into molten aluminum, stirring the melt to
homogenate, keep the molten aluminum static for 5~*0
minutes.
(5). Better use it after refining or before the last time of
refining.
4. Package and Storage:
Appearance: white metal nuggets.
**0g***0g/each bar
Storage
:Keep dry and ventilated