Sell tool steel L6 similar as 1.2714/1.2713, SKT4

Description

Typical application:
 Punches and dies, cold forming tools, and coining dies.
Heat Treatment:
Forge: at ***0?****5? Cool slowly and anneal then.
Annealing: Heating slowly and uniformly to **0~**0?, furnace cooling to **0? at a rate *0~*0?/h. Hardness max. HB **5
Stress Relieving: Heat to **0~**5?, furnace cooling.
Hardening: Heating to **0~**5?, holding *0 minutes per *5 mm. Quenchant: By oil.
Tempering: Heating to **5~**0?, holding *0 minutes per *5 mm. Air-cooling. Hardness HRC *2 to HRC *5