Description

~Item MZ*5 MZ**5
 Powder Oiled powder Granule Powder Oiled powder Granule
Appearance Light yellow powder(granule) Light yellow powder(granule)
Initial M.P. ℃ ≥ **0.0 **0.0 **0.0 **0.0 **0.0 **0.0
Loss on drying % ≤ 0.*0 0.*0 0.*0 0.*0 0.*0 0.*0
Zinc content % *6.***2.0 *6.***2.0 *6.***2.0 *5.***8.0 *5.***8.0 *5.***8.0
Free M % ≤ 5.0 5.0 5.0 *5.0 *5.0 *5.0
Residue on **0μm sieve % ≤ 0.*0 0.*0  0.*0 0.*0 
Residue on  *3μm  sieve % ≤ 0.*0 0.*0  0.*0 0.*0 
Additive %  1.**2.0   1.**2.0 
Granule Diameter mm   2.*0   2.*0
Properties: Light yellow powder (granule) with a little bitter, no poison. The density is 1.*0, the decomposable temperature is **0οC. Soluble in chloroform, acetone, partly soluble in benzene, ethanol, CCl4, insoluble in gasoline, water and ethyl acetate. Decomposion when meeting strong acid and strong alkali

Application: Used for NR,IR,SBR,NBR, EPDM and latex. May be regarded as an intermediate between WILLING M and WILLING DM. Used as a secondary accelerator in combination with WILLING PZ andWILLING EZ. Similar performance as WILLING MBT at curing temperature in dry rubber application. Has lower scorch and better processing safety. Suitable for mold curing. Require zinc oxide and stearic acid as activators in many kinds of rubber batch. Easily disperses in rubber; yields non-staining and non-discoloring products. Mainly used in the manufacture of latex products, foam rubber, latex coating gloves, etc