Description

   RTV2 silicone rubber for gypsum cornice mold making

• Vacuum pumping: After finishing the first step, then go to the vacuum pumping . Usually, there will be some air bubbles in the mixture during the mixing process working. So after the first step after finishing handling of the original mold, we need come to the vacuum pumping process.This step is better for taking less than 3-5 minutes. Otherwise, it will cause cross linking reaction, and no more further steps will be available. 
• Brushing cast or Perfusion Molding operation a.Carefully wash the original mold , then dry it with an air gun. Then brush some release agent such as soap water, detergent,vaseline,liquid wax ,etc.. b. Evenly brush the mixed silicon rubber on the product which is covered with mold spray with a brush or a brush pen. c. After the cross linking reaction (about 30 minutes), brush a second coat which can increase the tension and tear strength of the mold. d. Cover a glass cloth on it after another 30 minutes of a second cross linking reaction, and use a brush pen or a brush to avoid any interstices. e. Cover a third coat. (Note: if you have high requirements for the tension and the tear strength for the mold, please repeat step c and step d. Hence, the finished silicone moulds will have a good quality and a longer life, which can help you save cost and increase production efficiency.) 
• Operations for the external mold: a. Make a square frame with four pieces of wooden boards or rubber plates, then place the product which is covered with the finished silicon rubber mould in the middle. b. Slowly and evenly perfuse the gypsum into the square frame. Also you can brush the resin on the product which is covered with the finished silicon rubber mould with a brush or a brush pen. Repeat this process two or three time after the cross link reaction. 
• Pouring moulding: It is suitable for simple products with the smooth surface. Without any mold lines, which helps you save time and is easy for operation. Evenly and slowly perfuse the mixed silicone rubber into the square fram. After the cross linking reaction and the silicone rubber turns dry,you can take the products out. Thus, the mold has been done. (Note:we usaully use soft silicone rubber to make molds by perfusing, which is easy for demoulding and will not damage the product in the silicone molds.) Packaging, storage and 

• The RTV-2 silicone rubber is packed with vacuumed thick PE bag inside,and iron barrel (tin) outside, packing in 5 kg, 25 kg , 200 kg. Curing agent (catalyst, cross-linking agent or other additives) are packed with 1 kg, 25 kg plastic bottles or barrels . and the weight is 3-5% of total silicone.