Description

Refractory Cement CA*0:
A**0:
Al2O3: **- *5 %, Fe2O3: 2.5 % max, SiO2: 8 % max., CaO: *2 - *8 %, R2O: 0.4% max
Blaine: **0 m2/kg min, initial setting time: >*0min, final setting time:<6h,
Flexural strength: 3.0 MPa(6h),6MPa(1d),7MPa(3d)
Compressive strength: *0 MPa(6h),*5MPa(1d),*5MPa(3d)
A**0:
Al2O3: *0 - *0 %, Fe2O3: 2.5 % max, SiO2: 7 % max., CaO: *2 - *8 %, R2O: 0.4% max
Blaine: **0 m2/kg min, initial setting time:> *0min,final setting time:<6h,
Flexural strength: 3.0MPa(6h),6.5MPa(1d),7.5MPa(3d)
Compressive strength: *0MPa(6h),*0MPa(1d),*0MPa(3d)
A**0:
Al2O3: *5%min, Fe2O3: 2.5% max, SiO2: 6.5 % max., CaO: *2 - *8 %, R2O: 0.4% max
Blaine: **0 m2/kg min, initial setting time:> *0min,final setting time:<6h,
Flexural strength: 3.0MPa(6h),8MPa(1d),*0MPa(3d)
Compressive strength: *0MPa(6h),*0MPa(1d),*0MPa(3d)