Yttria Stabilized Zirconia
Beads are
manufactured from dry Yttria Stabilized Zirconia powder by high
compaction press. They was sintered at a high temperature to form a
Tetragonal Zirconia Polycrystal(Y-TZP) microstructure. The highest
bending strenghth and fracture toughness was considered the first
choice of grinding media to mill the most sensitive powder or
slurry.
Advantage:
1.Preventing material from contamination
because of its extreme low wear
rate.
2.High grinding
efficiency.
3.Lower total costs due to the long using
life.
User:
Materials for grinding and dispersed,
Structural Ceramics,
Electronics Ceramics, Refractory Ceramics,
Magnetic material, Metallurgy,
medicine,
food, cosmetics, paints, textiles, printing
and dyeing, pigment and other
industries.
Sizes:
Sphere:
1,1.5,2,2.5,3,5,7,*0…*5mm
Cylinder
3×3,5×5,7×7,*0×*0,*2×*2mm
Wear resistance compared with the other
grinding media:
| Composition | Wt% | *5%Zro2, 5%Y2O3 |
| Specific density | G / cm3 | ≥5.*5 |
| Hardness (HV)) | HRA | *0 |
|
Thermal
expansion Coefficient (*0~**0) |
(*0*6/k) | *1 |
| Elastic modulis | Gpa | **5 |
| Fracyure toughness | Mpa . m 1/2 | ***0 |
| Bending strength | Mpa | ***0 |
| Grain size | μm | 0.5 |
| Thermal conductivity | W / (m.k) | 3 |
| بلد: | China |
| نموذج رقم: | - |
| سعر فوب: | أحصل على آخر سعر |
| الموقع: | - |
| سعر الحد الأدنى للطلب: | - |
| الحد الأدني للطلب: | - |
| تفاصيل التغليف: | - |
| موعد التسليم: | - |
| القدرة على التوريد: | - |
| نوع الدفع: | - |
| مجموعة المنتج : | Zirconia Ball |