WuXi TecCeram Fine Ceramic Co., Ltd

9mol% Magnesia partially stabilized zirconia; Density: >5.7g/cm3; Bending strength: >500MPa; Hardness (HV0.5): >1100; Fracture Toughness:

Silicon nitride with very low friction factor because of its special self-lubricating property. The microstructure consists of elongated crystals that

Zirconia naturally occurs in the form of the mineral baddeleyite. For ceramics purposes, however, it is extracted from zirconium sand and other minera

High purity silicon nitride rod; Density: >3.2 g/cm3; Bending strength: >750MPa; Hardness (HV0.5): >1700; Fracture Toughness: >6.7MPam1/2

material: a-Al2O3 purity: 99.7% density:3.9g/cm3 bending strength:380MPa hardness (HV0.5): 2000 max. using temperature:1700degree C

Zirconia pins are produced by CIP plus grinding. Here are major properties: Density: >6.02 g/cm3; Bending strength: >800 MPa; Toughness: >8MPam1/2;

High purity alumina (99.5%~99.9%) rod; Density: >3.93 g/cm3; Bending strength: >350MPa; Hardness (HV0.5): >1900; Dimension: 0.5mm~50mm wit

High purity silicon nitride rod; Density: >3.2 g/cm3; Bending strength: >750MPa; Hardness (HV0.5): >1700; Fracture Toughness: >6.7MPam1/2

Aluminum titanate material is produced in a special sinter process from high grade raw materials. During this well defined reaction process, a micropo

Zirconia pins are produced by CIP plus grinding. Here are major properties: Density: >6.04 g/cm3; Bending strength: >1000 MPa; Toughness: >8MPam1/2