Yangquan Jintu Refractory Materials CO.Ltd

SiO2 Content (%) 9% Al2O3 Content (%) 85% min Refractoriness (Degree) 1770°< Refractoriness&

SiO2 Content (%) 6% max Al2O3 Content (%) 88% min Refractoriness (Degree) 1770°< Refractorin

Al2O3 Content (%) 85% min MgO Content (%) 0.25% max CaO Content (%) 0.25% max Fe2O3 ≤2%

SiO2 Content (%) 12% max Al2O3 Content (%) 80% min Refractoriness (Degree) 1770°< Refractori

SiO2 Content (%) 12% max Al2O3 Content (%) 80% min Refractoriness (Degree) 1770°< Refractori

Application in ceramics industry Grade kaolin clay AL2O3 45% min SIO2 47-48% FE2O3 1.2% max Bulk den

SiO2 Content (%) 12% max Al2O3 Content (%) 80% min Refractoriness (Degree) 1770°< Refractori

Place of Origin Shanxi, China (Mainland) Brand Name JINTU Model Number M-1.2 Al2O3 65%min Fe2O3 1.6%ma

Al2O3 Content (%) 87% min MgO Content (%) 0.25% max CaO Content (%) 0.25% max Refractoriness (Degree) 17

Sintered mullite M70 AL2O3: 70-73% SIO2:22.5-25.5% TIO2: 2.7% max FE2O3: 1.5%max CaO MgO: 0.35%max k2O N

Application in paper, plastic, paint industry Grade kaolin AL2O3 45 /-2% SIO2 52 /-2% FE2O3 0.5% Max

SiO2 Content (%) 12% max Al2O3 Content (%) 80% min MgO Content (%) 0.2% max CaO Content (%) 0.2% max R

SiO2 Content (%) 48-50% Al2O3 Content (%) 45% min Fe2O3 0.8% max TiO2 2.5% max Bulk density 2.4g/cm3 m

Al2O3 Content (%) 88% min MgO Content (%) 0.25% max CaO Content (%) 0.25% max Fe2O3 ≤1.

Material Mullite SiO2 Content (%) 42.98% Al2O3 Content (%) 50%min MgO Content (%) 0.2 min CaO Content

Material Castable Al2O3 Content (%) 60%min Refractoriness (Degree) Common (1580°< Refractori

Place of Origin Shaanxi, China (Mainland) Material Castable Al2O3 Content (%) 60%min Refractoriness (Deg

ITEM AL2O3 FE2O3 TIO2 K2O Na2O CaO MgO Bulk density GJ75 ≥75 ≤2.5 &acir

Place of Origin Shanxi, China (Mainland) Brand Name JINTU Model Number M-1.2 Al2O3 65%min Fe2O3 1.6%ma

Material Mullite Al2O3 Content (%) 62-65% Refractoriness (Degree) 1770°< Refractoriness<